Titanium Alloy Grade 9 / Ti-3Al-2.5V

Technical Data Sheet

Chemical Composition Limits
Weight %	Ti	C	Fe	N	Al	O	V	H	Y	Other
Titanium Ti3Al2.5V	bal	0.05	0.30	0.02	2.5 / 3.5	0.12	2.0 / 3.0	0.015	0.005	0.40 total

Titanium Ti3Al2.5V (grade 9) or more simply known as Ti-3-2.5 is commonly grouped with the commercially pure grades due to it's ability to be cold rolled. The strength of Ti3al2.5V (Ti-3-2.5) falls between Grade 4 and Grade 5 . However Ti3Al2.5V (grade 9) can be used at higher temperatures than Grade 1, Grade 2, Grade 3 and Grade 4. Applications for Ti3Al2.5V are Aerospace, Chemical Processing, Medical, Marine, Automotive industries etc.

Typical Mechanical Properties

Material	Tensile Strength min		Yield Strength min		Elongation (%)
	ksi	Mpa	ksi	MPa
Titanium Alpha-Beta Alloy Ti-3Al-2.5V	90	621	75	517	15
Ti-3Al-2.5V Hydraulic Seamless Tubing (annealed)

Availability
Titanium Ti3Al2.5V (Ti-3-2.5) is available in Bar, Tube, Strip, Coil, Sheet and Plate. For all stock and size availability contact Sales.

Specifications
ABS 5004
ABS 5141
AMS 4943 Hydraulic Seamless Tubing
AMS 4944 Hydraulic Seamless Tubing
AMS 4945 Hydraulic Seamless Tubing
B 265, ASTM B337 Gr9, ASTM B338 Gr9 & ASTM B381 Gr9
UNS R56320
AMS-T-9046 AB-5 Sheet, Strip, Plate
AMS-T-9047 3Al-2.5V Bar
MIL-T-9046J AD-5 Sheet, Strip, Plate
MIL-T-9047 3AL 2.5V Bar

Customer Reviews - What Customers Say About Us!

"I would like to extend my gratitude to the entire staff at Aircraft Materials. It is a true pleasure to work with professionals in the aerospace industry. Keep up the great work!"

"Thank you very much, everything seems perfect. The quality of your cutting is superb."

"Could not fault your service."

"The service was perfect you had stock and same day collection"

"Item was very well packed"

CLICK HERE TO VIEW OUR BROCHURE

Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.