Part Number WS 1.4105
Technical Data Sheet
CCV-120 is a chromium and vanadium alloyed silver steel material which is manufactured in Rod, Bar and Coil.
| Chemical Composition Limits | ||||||
| Weight % | C | Cr | Mn | V | Si | Fe |
| CCV-120 | 1.10-1.25 | 0.50-0.80 | 0.20-0.40 | 0.07-0.12 | 0.15-0.30 | Rem |
| Other Chemically similar Specifications | ||||||
| Weight % | C | Cr | Mo | Mn | S | Fe |
| WS 1.2210 | 1.10-1.25 | 0.50-0.80 | 0.20-0.40 | 0.07-0.12 | 0.15-0.30 | Rem |
| DIN 115 CrV3 | 1.10-1.25 | 0.50-0.80 | 0.20-0.40 | 0.07-0.12 | 0.15-0.30 | Rem |
| AISI A681 / L2~ | 1.10-1.25 | 0.50-0.80 | 0.20-0.40 | 0.07-0.12 | 0.15-0.30 | Rem |
| EN107CrV3~ | 1.10-1.25 | 0.50-0.80 | 0.20-0.40 | 0.07-0.12 | 0.15-0.30 | Rem |
(AISI A681 /L2 Chromium and Vanadium Alloyed Silver steel, WS 1.2210 Chromium and Vanadium Alloyed Silver steel)
Material Features
Alloyed steel with best hardening properties and reduced critical cooling rate. CCV-120 Cr V is characterised by a lower risk of stress cracking and distortion this alloy is relatively insensitive to overheating.
Available in
Cold drawn and polished; 10-35kg/coil
Bars Ø 0-3.50 mm cold drawn and polished
Bars Ø 3.50-40mm cold drawn, ground and polished.
Standard length of bars 2m Surface roughness N6
Tensile Strength
about 750 N/mm2 (before heat treatment)
Standard tolerance
Diameter ISO h8
Out of roundness/ eccentricity 1/2 of dia. tolerance.
Heat treatment
Hardening water 800-820ºC above Ø 10mm
Oil: 820-840ºC up to Ø 10mm
Cutting rate
15-25m/min (dependent on lubrication oil, the cutting tools, the form of parts)
Stock Range
Ø 1.00-40.00mm
For all stock and size availability contact Sales.
Return to Main Precision Ground Material