Part Number WS 1.4034+S
Technical Data Sheet
Chronifer Labor M-13 is a hardenable alloyed free cutting stainless steel which is manufactured in rod, bar and coil. (AISI 420F ~ Stainless Steel).
| Chemical Composition Limits | |||||||
| Weight % | C | Si | Mn | Cr | S | Mo | Fe |
| CHRONIFER LABOR M-13 | 0.40-0.50 | 1.60 max | 1.00 max | 12.50-14.50 | 0.20 max | 0.60 max | Rem |
| Other Chemically similar Specifications | |||||||
| Weight % | C | Si | Mn | Cr | S | Mo | Fe |
| WS 1.4034 + S | 0.40-0.50 | 1.60 max | 1.00 max | 12.50-14.50 | 0.20 max | 0.60 max | Rem |
| DIN X 46 CrS 13 | 0.40-0.50 | 1.60 max | 1.00 max | 12.50-14.50 | 0.20 max | 0.60 max | Rem |
| AISI 420F~ | 0.40-0.50 | 1.60 max | 1.00 max | 12.50-14.50 | 0.20 max | 0.60 max | Rem |
Material Properties
This product is a compromise between good machinability (S-Content), high wear resistance (Cr-content) and possibility for hardening (C-Content. Chronifer Labor M 13 resists to corrosion after tempering and a forced polishing of the parts.
Availability
Coils: cold drawn and polished, 10-35kg/coil
Bars: 0-1.99 mm: cold drawn and polished
Bars: 2.00-40mm: cold drawn, ground and polished
Bars length: 2m or 3m surface roughness N5-N6
Standard Tolerances
Diameter: ISO h8 (Ø 3-10mm h7)
Length of bars: +/- 30mm
Out of Roundness/eccentricity: 1/2 of diameter
Heat Treatment
Soft annealing: 750-800C slow furnace cooling (2-4 hours)
Hardening: 1000-1050 C
Max obtainable hardness 55 HRC
Cutting Rate
40-55 m/min (approximate value, depending on the lubrication, the cutting tools, the shape of parts)
For all stock and size availability contact Sales.
Return to Main Precision Ground Material
Customer Reviews - What Customers Say About Us!
| CLICK HERE TO VIEW OUR BROCHURE |
Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.