Stainless Steel ER 320LR


Technical Data Sheet

 

Chemical Composition Limits
Weight% C Mn Si Cr Ni S P Cb+Ta Mo Cu
ER 320LR 0.025 max 1.5-2.0 0.15 max 19-21 32-36 0.02 max 0.015 max 8X C min / 0.4 max 2-3 3-4

Alloy ER 320LR has a composition similar to Alloy ER320, except that carbon, silicon, phosphorus and sulfur levels are kept at lower levels as well as the columbium and manganese being specified at a narrower range. The low melting residuals are limited in this alloy to reduce the possibility of micro fissuring. It is for this reason that the alloy ER320 LR is often used for welding Type 320 stainless steels.

Typical Mechanical Properties

Material Ultimate Tensile Strength Offset Yield Strength 0.2 % Elongation (%)
psi MPa psi MPa
ER 320LR 86,000 590 57,500 400 35


Availability
Alloy ER 320LR is a Stainless Steel TIG, MIG and SUB-ARC wire used for welding. For all stock availability contact Sales.

Specifications
AWS 5.9
ASME SFA 5.9
AWS ER 320LR
UNS N08022