Cobalt Alloy 25/ Haynes © Alloy 25/ Udimet L605/ Alloy L-605

Technical Data Sheet

Udimet Alloy L-605 / Haynes Alloy 25 is a solid solution strengthened cobalt-chromium-tungsten nickel alloy which combines excellent high temperature strength and oxidation resistance to 2000°F with good resistance to sulfidation, wear and galling. Alloy L-605 / Alloy 25 has good forming characteristics and is capable of being forged, hot worked or cold worked, althoug it does work-harden very rapidly so frequent intermediate annealing treatments are recommend for complex forming operations. Alloy 25 / L-605 can also be readily welded by most conventional welding methods using similar composition welding wire (AMS 5796) or coated electrodes (AMS 5797). Alloy L-605 / Alloy 25 is supplied solution heat treated in the range of 2150-2250°F and rapid air or water quenched to attain optimum properties. Alloy L-605 / Alloy 25 has many applications in military and commercial gas turbine engine components such as rings, blades and combustion chamber parts although for many modern engines it has largely been replaced by Alloy 188 or Alloy 230.

Chemical Composition Limits
Weight%	C	P	Si	Ni	W	Mn	S	Cr	Co	Fe
Alloy L-605	0.05 - 0.15	0.040 max	0.40 max	9.0 - 11.0	14.0 - 16.0	1.0 - 2.0	0.030 max	19.0 - 21.0	Bal	3.0 max

Typical Mechanical Properties

Material	Temperature °F	Yield Strength 0.2%	Tensile Strength	Elongation (%)	Hardness HB
Extruded Bar Alloy 25 / L-605	RT	310 Mpa 45 KSI	862 Mpa 125 KSI	30	277 max

Material Sheet	Thickness (inches)	Yield Strength 0.2% KSI	Tensile Strength KSI min	Elongation (%)	Hardness HRC
Alloy 25 / L-605 Solution Treated (AMS 5537)	0.005-0.020	55-80	130	30	-
Alloy 25 / L-605 Solution Treated (AMS 5537)	0.020-0.032	55-80	130	35	-
Alloy 25 / L-605 Solution Treated (AMS 5537)	0.032-0.043	55-80	130	40	-
Alloy 25 / L-605 Solution Treated (AMS 5537)	0.043-0225	55-80	130	45	-

Availability
Alloy L-605 (Haynes © Alloy 25) is available in Bar (Rounds), Rod, Wire, Sheet, Strip, Forging Stock, Foil, Welding Wire, Billet and L- 605 Vac Melt Bar. For all stock availability contact Sales.

Specifications
UNS R30605
AMS 5537 Sheet Strip and Plate
AMS 5759 Bar and Forging Stock
AMS 5796 Welding Wire
AMS 5797 (UNS W73605) Welding Rod
ASTM F90 Bar and Wire (surgical implant quality)
GE B50T26
GE B50A460
Tradenames: Udimet Alloy L-605, Haynes 25, Nickelvac L-605

Customer Reviews - What Customers Say About Us!

"Just wanted to say thanks for your efforts and updates"

"I always try you as you often keep stock that can't be found elsewhere"

"Prompt answer & knowledge of available material, timescale & price within a good time"

"Packaging is superb"

"Thank you for your quick response"

CLICK HERE TO VIEW OUR BROCHURE

Disclaimer
Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.