Stainless Steel ER 2594

Technical Data Sheet


Chemical Composition Limits
Weight% C Cr Ni Mo Mn Si P S N Cu W
ER 2594 0.03 max 24-27 8-10.5 2.5-4.5 2.5 max 1 max 0.03 max 0.02 max 0.20-0.30 1.5 max 1.0 max

Alloy ER 2594 is a superduplex welding wire. The Pitting Resistance Equivalent Number (PREN) is at least 40, thereby allowing the weld metal to be called a superduplex stainless steel. This welding wire provides matching chemistry and mechanical property characteristics to wrought superduplex alloys such as 2507 and Zeron 100 as well as superduplex casting alloys (ASTM A890). This welding wire is overalloyed 2-3 percent in Nickel to provide optimum ferrite/austenite ratio in the finished weld. This structure results in high tensile and yield strength along with superior resistance to SCC and pitting corrosion.
Set the parameters to obtain a heat input of 10,000 -30,000 Joules/inch. Pre-heat is not required. The interpass temperature should be maintained at 300ºF max. If post weld annealing is required this weld metal will require a higher annealing temperature than that required by the duplex base metal.

Alloy ER 2594 is a Stainless Steel TIG, MIG and SUB-ARC wire used for welding. For all stock availability contact Sales.

AWS 5.9
AWS ER2594
UNS S32750

Return to Main Welding Page

Customer Reviews - What Customers Say About Us!

"I would like to extend my gratitude to the entire staff at Aircraft Materials. It is a true pleasure to work with professionals in the aerospace industry. Keep up the great work!"
"Thank you very much, everything seems perfect. The quality of your cutting is superb."
"Could not fault your service."
"The service was perfect you had stock and same day collection"
"Item was very well packed"

Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.